PE Colour Coated Sheets3003, 5052

PE colour coated sheets3003, 5052 Signi PE prepainted Aluminum coil is processed through the technics of roller coating and baking with precise polyester paints. Its color is glossy and with variety of colors enabling you to choose easily. Chromatic aberration is small, impact resistance is strong and easy to be processed, and all PE prepainted Aluminum coil its performance has reached or surpassed the national criteria. The products are widely used in indoor and door decoration, ceilings, room surface tiles, corrugated boards, wall panels, advertisement boards, counters, home appliances, decoration in and out of autos and boats. AlloyThicknessWidthcoil  weight1100, 8011, 3003, 5052,   and  other  alloy0.1mm_2.5mm20mm_1850mm< 3MTPE  coatingPE  (polyester)  coating:   Using  high  molecular  polymer  as  monomer  and  addition  of  alkyd,   this  pe  coating  method  of  our  color  coated  aluminum  coil  is  an  UV-resistant  coating.   It  can  be  classified  matt  and  glossy  according  to  coating  gloss.   The  compact  molecule  structure  makes  paint  surface  luster  and  smooth,   which  assures  good  printing  on  the  PE  coated  aluminum  coils  surface.   With  an  warranty  of  8-10  years  for  weather  resistance,   it  is  specially  applied  for  internal  decoration  and  sign  board.Color    Match For  custom'   color  requests,   we  can  deal  as  following:  1.   Supply  a  physical  sample  of  custom  color.   A  color  sample  on  metal  is  preferred.   If  other,   it  is  also  acceptable.   But  the  color  matching  rate  may  be  not  good  as  color  on  metal.  2.   New  color  sample  is  usually  offered  by  our  paint  supplier  in  5-7  days,   special  color  should  be  in  7-10  days.  3.   Upon  receipt  of  color  sample,   please  approve  in  writing  as  soon  as  possible.   Once  you  approved,   we  will  arrange  purchasing  and  production.  Note:   Color  difference  maybe  occurred  in  different  production  batch,   so  it  is  suggested  all  panels  are  placed  in  one  order  for  same  project.   And  keep  same  direction  as  arrow  on  protective  film  when  installing  to  avoid  any  color  difference  by  vision  1)  Thickness≤ 0.5mm ItemTest  ItemStandardNational  standardTest  Result1 Color  Difference ECCA  T3 Δ E≤ 2.0 Δ E≤ 1.5 2 Gloss  Difference ECCA  T2 ≤ 10 ≤ 5 3 Coating  Thickness ECCA  T1 Min  14µ m ≥ 16µ m 4 Pencil  Hardness ASTM  D3363 ≥ HB HB 5 T-bend ASTM  D4145 ≤ 3T ≤ 2T 6 Adhesion ASTM  D3359 Grade  0 Grade  0 7 Impact ASTM  D2794 ≥ 20kg. cm ≥ 20kg. cm 8 Boiling  water  Resistance GB/T17748 2h  no  change 2h  no  change 9 Solvent  Resistance ASTM  D2248 200  times  paint  remaining 200  times  paint  remaining 10 Salt  Resistance ASTM  B117 720  hrs≤ grade  1 720hrs≤ grade  1 11 Dirt  Resistance GB/T9780 ≤ 5% < 5% 12 Color  retaining GB/T16259 600hrs E≤ 2.0 E≤ 2.0 13 Gloss  weaken  Level 600hrs  ≤   grade  2 600hrs  ≤   grade  2 14 Chalking 600hrs  No  Change No  Change 2)  Thickness> 0.5mm  ItemTest  ItemStandardNational  standardTest  Result1 Color  Difference ECCA  T3 Δ E≤ 2.0 Δ E≤ 1.5 2 Gloss  Difference ECCA  T2 ≤ 10 ≤ 5 3 Coating  Thickness ECCA  T1 Min  14µ m ≥ 18µ m 4 Pencil  Hardness ASTM  D3363 ≥ HB HB 5 T-bend ASTM  D4145 ≤ 3T ≤ 2T 6 Adhesion ASTM  D3359 Grade  0 Grade  0 7 Impact ASTM  D2794 ≥ 50kg. cm ≥ 50kg. cm 8 Boil  Resistance GB/T17748 2hrs    No  change                     2hrs    No  change           9 Solvent  Resistance ASTM  D2248 200  times    paint  remaining       200  times  paint  remaining                         10 Salt  Resistance ASTM  B117 720hrs  ≤   grade  1                                 720hrs  ≤   grade  1           11 Acidity  ResistanceGB/T9780 ≤ 5% < 5% 12 Color  retention GB/T16259 600hrs E≤ 2.0 E≤ 2.0 13 Gloss  weaken  Level 600hrs  ≤ grade  2   600hrs  ≤   grade  2               14 Chalking     No  change                                   No  change           /* January 22, 2024 19:08:37 */!function(){function s(e,r){var a,o={};try{e&&e.split(",").forEach(function(e,t){e&&(a=e.match(/(.*?):(.*)$/))&&1